一、            PTFE微孔薄膜簡介Introduction to PTFE Microporous Membrane

PTFE微孔薄膜由高結(jié)晶度的PTFE分散料，經(jīng)過擠壓、縱向拉伸、橫向拉伸，最終形成帶有立體三維結(jié)構(gòu)的薄膜。其孔徑在0.02～5um之間，薄膜厚度在8～30um，孔隙率在80～97%之間。

PTFE micro-porous membrane is made up of high crystallinity PTFE fine powder and shaped into 3D structure through compressing, vertical and horizontal stretching. The membrane pore size is between 0.02~5μm, thickness is 8~30μm and porosity is between 80~97%.

 

 

金由iTEX高性能PTFE微孔薄膜特點

金由iTEX高性能PTFE微孔薄膜在生產(chǎn)之初，嚴(yán)格控制PTFE分散料品質(zhì)。配合18年P(guān)TFE微孔薄膜的生產(chǎn)經(jīng)驗，在生產(chǎn)過程中，對于細(xì)節(jié)精益求精。加上多處“獨到”的生產(chǎn)工藝，使金由iTEX高性能PTFE微孔薄膜具有高耐水壓力、高透濕性、高機械強度等性能。

 

Features of Jinyou iTEX PTFE membrane

The PTFE fine powder is controlled strictly before to be used as approved material.  

And thanks to our 18-year experience and unique technology in producing PTFE membrane, we have consistently improved the product in every detail.

Therefore, iTex membrane is featured by high water resistance, high breathability and high durability.

 

 

高耐水壓力：在20次水洗以后，按美國ASTM D751-2006標(biāo)準(zhǔn)測定：C型達20,000mm耐水壓力。S型可達67,000mm耐水壓力，已達美國MIL-DTL-31011B水平（美國軍方標(biāo)準(zhǔn)），特別適用于軍、警、消防官兵服裝。

High Water Resistance

According to ASTMD7751-2006, water resistance for type C reaches 20,000mm H₂O and Type S reaches up to 67,000mm H₂O after 20 times washing, which meets the standard of US MIL-DTL-31011B. Therefore, it becomes ideal material to make uniforms for army, police and firefighting.

 

高透濕/透氣性：洗滌前透濕量（汗液形成的水蒸氣）按日本標(biāo)準(zhǔn)JISL099B1標(biāo)準(zhǔn)測試，C型達5000g/m²·24h以上,S型達7500g/m²·24h以上。

High breathability / Air Permeability

According to JISL099B1, the moisture breathability for Type C reaches over 5000g/m²·24h and Type S over 7500g/m²·24h before washing.

 

高耐用性：金由iTEX高性能PTFE微孔薄膜，由于在生產(chǎn)過程經(jīng)過的特殊的處理，使其具有極好的防油污性能。即使多次洗滌劑水洗后，仍具有高耐水壓優(yōu)點。解決了目前中國國內(nèi)市場上一般PTFE面料，經(jīng)水洗后耐水壓急劇下降的難題，使用壽命大大延長。

High Durability

Jinyou iTEX PTFE membrane has excellent oil and stain repellence due to special treatment. It also maintains high water resistance after being washed many times by detergent.

In contrast, water resistance from other companies’ membrane garment in Chinese market still drops dramatically after being washed.

So Jinyou iTEX PTFE membrane can greatly extend the service life and be a leader in the market.

 

a)         

二、            金由iTEX高性能微孔薄膜復(fù)合織物性能指標(biāo)

試驗項目Item   產(chǎn)品Product	耐水壓力Water Pressure Resistance（mmH2O）				透濕量S Breathability （g/m2·24h）
	初始μ Initially	水洗20次后μ After Wash	初始u Initially	水洗20次后u After wash
一般PTFE膜 Other Membrane	～10,000	~3,000	～5,000	1,000	~5,000
iTEX -C	≥35,000	≥20,000	≥20,000	≥15,000	≥7,500
iTEX -S	≥75,000	≥63,000	≥63,000	≥50,000	≥5,500

μ依據(jù)ASTM 0751-2006美國標(biāo)準(zhǔn)；As per ASTM 0751-2006

u依據(jù)JISL 1092 日本標(biāo)準(zhǔn)；As per JISL 1092

S 依據(jù)JISL 1099測試As per JISL 1099

 

三、            金由iTEX-S型PTFE微孔薄膜復(fù)合織物與美國軍用標(biāo)準(zhǔn)比較

Comparative data between Jinyou iTEX-S type and US Military Standards

 

產(chǎn)品用途 Product Application

防火防護布料 Protective Clothing for firefighing

戶外（防寒）服 Outdoor Clothing

 

在其他領(lǐng)域的應(yīng)用 Other Products Application In Different Area

a)      PTFE scrim is being used in power station to secure 30,000 hours service life. Market share is over 50%.

b)       100% PTFE felt with PTFE membrane is being used in incineration to secure 4 years service life and emission below 10mg/Nm³. Market share reaches up to 50%.

c)       iHEPA high efficient PSB filter paper is being used for HEPA filter and cartridge in China as the first choice.

d)       iGasket expanded Gasket will break the monopoly from an American company in Chinese market for 15 years.